Flux sous arc submergé - ELIFLUX BFPV
Désignation Normalisée
| TS EN ISO 14174 | SA FB 1 66 AC H5 |
|---|---|
| EN ISO 14174 | SA FB 1 66 AC H5 |
| AWS A5.17 | F7A2-EM12/F7A2-EM12K |
| AWS A5.23 | F8A4-EA2-A2/F8A5-EA4-A3/ F11A8-EM4(mod)-M4 |
Analyse Chimique du Type Métal Déposé (%)
| SAW - Wire | C | Si | Mn | Mo | Cr | Ni |
|---|---|---|---|---|---|---|
| S2 | 0.06 | 0.35 | 1.20 | --- | --- | --- |
| S2 Si | 0.07 | 0.40 | 1.25 | --- | --- | --- |
| S2 Mo | 0.07 | 0.40 | 1.30 | --- | --- | --- |
| S3 Mo | 0.05 | 0.30 | 1.75 | 0.50 | --- | --- |
| S3 NiCrMo 2.5 | 0.06 | 0.40 | 1.75 | 0.50 | 0.40 | 2.10 |
Caractéristiques Mécaniques du Métal Déposé
| SAW Wire | AWS A5.17 / AWS A5.23 | Yield Strength (N/mm²) | Tensile Strength (N/mm²) | Elongation (L0=5d0) (%) | Résilience (ISO-V/-30°C) | Resilience(ISO-V/-40°C) | Résilience (ISO-V/-50°C) | Résilience (ISO-V/-60°C) |
|---|---|---|---|---|---|---|---|---|
| S2 | F7A2-EM12 | 430 | 520 | 29 | 60 J | --- | --- | --- |
| S2 Si | F7A2-EM12K | 440 | 515 | 30 | 65 J | --- | --- | --- |
| S2 Mo | F8A4-EA2-A2 | 490 | 595 | 26 | --- | 60 J | --- | --- |
| S3Si | F8A5-EA4-A3 | 500 | 588 | 27 | --- | 100 J | 80 J | --- |
| S3NiCrMo2.5 | F11A8-EM4(mod)-M4 | 700 | 775 | 23 | --- | 55 J | 45 J | min.27 J |
Fonctions Et Applications
- Flux a forte basicité
- C’est un flux à arc submergé de type Floride basique
- Faible taux en hydrogène et de forte résilience
- Préconiser dans les processus tandem et pour des aciers de faibles épaisseurs avec des espaces de soudage étroits Adéquat dans la fabrication des réservoirs à pression Le flux devra être étuvé entre 300 et 350°C pendant 2 h avant utilisation
Basıcıte
| Basicity | 2.8 |
|---|
Intensités Moyennes & Poids
| Produit Code | Package Poids (Kg) | Conditionnement |
|---|---|---|
| 6010800016 | 25 | Kraft Bag |