Flux sous arc submergé - ELIFLUX BSS-A
Désignation Normalisée
| TS EN ISO 14174
|
SA FB 2 65 DC |
| EN ISO 14174
|
SA FB 2 65 DC |
Analyse Chimique du Type Métal Déposé (%)
| SAW - Wire |
C |
Si |
Mn |
Mo |
Cr |
Ni |
P |
S |
| ELOX UP 307 |
0.08 |
0.90 |
6.50 |
--- |
19.0 |
9.0 |
--- |
--- |
| ELOX UP 308 L |
0.03 |
0.54 |
1.57 |
--- |
19.20 |
9.30 |
--- |
--- |
| ELOX UP 309 L |
0.03 |
0.40 |
1.63 |
0.03 |
24.20 |
13.10 |
--- |
--- |
| ELOX UP 316 L |
0.03 |
0.40 |
1.73 |
2.13 |
19.00 |
11.20 |
--- |
--- |
Caractéristiques Mécaniques du Métal Déposé
| SAW Wire |
Standards |
Tensile Strength (N/mm²) |
Elongation (L0=5d0) (%) |
Résilience (ISO-V/0°C) |
Résilience(ISO-V/-110°C) |
Résilience (ISO-V/-196°C) |
| ELOX UP 307 |
AWS A5.9 : ER 307 |
620 |
32 |
--- |
37 J |
- |
| ELOX UP 308L |
AWS A5.9 : ER 308 L |
550 |
41 |
70 J |
50 J |
58 J |
| ELOX UP 309L |
AWSA5.9: ER 309 L |
540 |
35 |
--- |
--- |
- |
| ELOX UP 316 L |
AWS A5.9: ER 316 L |
570 |
39 |
60 J |
50 J |
35 J |
Fonctions Et Applications
- C’est un flux aggloméré florit-basique., généralement utilise pour le soudage des aciers inoxydables,
- pour le rechargement le flux peut aussi être utiliser.Très résistant à la corrosion et grande
- résistance mécanique
- Avant l’utilisation le flux doit être étuvé à 350 °C pendant 2 heures
- Formation of easily-removable slags
- Requirement of re-drying at 300-350°C for 2 hours
Basıcıte
Intensités Moyennes & Poids
| Produit Code |
Package Poids (Kg) |
Conditionnement |
| 6010800014 |
25 |
Kraft Bag |