Paslanmayan Polad Elektrod - ELOX RS 307
Normaları
| EN ISO 3581-A
|
E Z 18 9 MnMo R 5 3 |
| TS EN ISO 3581-A
|
E Z 18 9 MnMo R 5 3 |
| AWS A5.4
|
~E307-26 |
Qaynaq Metalının Tərkibi % (Standart)
| C |
Si |
Mn |
Cr |
Ni |
Mo |
| 0,07 |
0,9 |
5,6 |
19,0 |
8,5 |
0,75 |
Qaynaq Edilə bilən Poladlar
- Dissimilar joints, tough buffer and intermediate layers prior to hardfacing, 14Mn-steels, 13 – 17% Cr and heat resistant Cr and austenitic steels up to 850ºC, armor plates, high carbon and quenched and tempered steels, surfacing of gears, valves, turbine blades, etc. For joint welding of unalloyed / low-alloyed or Cr steels with high-alloyed Cr and CrNi-steels. Welding of austenitic high manganese steels and with other steels.
Mexaniki Dəyərlər
| Axın Gücü (N/mm2) |
Gərilmə Gücü (N/mm2) |
Çarpi təsir testi üzrə gücü (ISO-V/+20°C) |
Uzanma (L0=5d0) (%) |
| min.400 |
590 - 700 |
min.47J |
min.35 |
İstifadə Edildiyi Yerlər Və Xüsusiyyətləri
- Welding of high resistant alloyed / unalloyed steels, heat-resistant steels / stainless steels, steels with 14% Mn, for welding problematic steels
- Joint and filler welding of different metals
- Rutile coated electrode, weld metal is austenitic, resistant to thermal shocks, keeps its toughness down to -100°C
- Requirement of re-drying for min. 2 hours at the temperatures between 120°C and 200°C
Axın Növü
Qaynaq Modelləri
Əməliyyat Məlumatları
| Məhsul Kodu |
Diam. x Hünd. (mm) |
Diam. x Hünd. (inch) |
Axın Gücü (A) |
Ağırlıq g / 100 Ədəd |
| 3010100943 |
ø3,2 x 350 |
ø1/8 x 14 |
110 - 150 |
4900 |
| 3010100948 |
ø4,0 x 350 |
ø5/32 x 14 |
140 - 180 |
7830 |
| 3010100953 |
ø5,0 x 350 |
ø3/16 x 14 |
180 - 220 |
11700 |