Low Hydrogen Electrode - LASER B 47-A
Standards
| TS EN ISO 2560-A
|
E 42 4 B 3 2 H5 |
| EN ISO 2560-A
|
E 42 4 B 3 2 H5 |
| AWS A5.1
|
E7016-1 H4 |
Chemical Composition of Weld Metal % (Typical)
Typical Base Material Grades
- S235JR-E295, E335, S235J2G3-S355J2G3, S235JRS1, S235J4S, S315G1S-S355G3S, S255N-S355N
- C22, C35
- P235T1-P355T1, P235T2, P355T2,
- L210-L360, L290MB-L320MB, API 5L: GrA, GrB, X42, X46, X52, X56, X60
- P235G1TH, P255G1TH, P235GH-P295GH
- GE200-GE300
Mechanical Properties
| Yield Strength (N/mm²) |
Tensile Strength (N/mm²) |
Impact Strength (ISO-V/-46°C) |
Elongation ((Lo=5do) (%)) |
| min. 420 |
500-610 |
min. 47 J |
min. 24 |
Features and Applications
- Suitability for welding with AC power
- Suitability for use in out-of-position welding except for welding at vertical down position
- Excellent strength and toughness
- Suitability for use in the fields of steel constructions, boiler, container, machine manufacturing, and shipbuilding construction as well as for use in welding low-purity and high-carbon steels
- Suitability for the formation of welding buffer layers when building up high-carbon steels
- Weld deposits with very low hydrogen content
- Weld metal recovery of about 125% with thick coating.
- Requirement of redrying for minimum 2 hours at the temperatures between 300°C and 350°C
Current Type
Welding Positions
Operating Data
| Product Code |
Diametré x Length (mm) |
Diameter x Length (inch) |
Welding Current (A) |
Weight g / 100 pcs |
| 3010100372 |
ø2,5 x 350 |
ø3/32 x 14 |
80 - 100 |
2320 |
| 3010100375 |
ø3,2 x 350 |
ø1/8 x 14 |
100 - 140 |
3720 |
| 3010100378 |
ø4,0 x 350 |
ø5/32 x 14 |
130 - 190 |
5380 |
| 3010100381 |
ø4,0 x 450 |
ø5/32 x 18 |
130 - 190 |
6820 |
Approvals