Low Hydrogen Electrode - OPUS 9 CM
Standards
| TS EN ISO 3580-A | E CrMo9 B 4 2 H5 |
|---|---|
| EN ISO 3580-A | E CrMo9 B 4 2 H5 |
| AWS A5.5 | E8018-B8 H4 |
| AWS A5.4 | E505-15 |
Chemical Composition of Weld Metal % (Typical)
| C | Si | Mn | Cr | Mo |
|---|---|---|---|---|
| 0,07 | 0,4 | 0,7 | 9,0 | 1.0 |
Typical Base Material Grades
- X12CrMo9-1, X7CrMo9-1
- GX12CrMo10
Mechanical Properties
| Yield Strength (N/mm²) | Tensile Strength (N/mm²) | Impact Strength (ISO-V/+20°C) | Elongation ((Lo=5do) (%)) | Heat Treatment |
|---|---|---|---|---|
| min. 460 | min. 590 | min. 34 J | min. 19 | 760 ±20 °C / 2h / furnace down to 300°C / cooling at (air) |
Features and Applications
- Welding of boilers, pressure vessel steels, pipe steels and cast steels
- Electrode coating of basic character
- Electrode content of % 9 Chromium, % 1 Molybdenum
- Resistance of weld metal to working temperatures up to 650°C
- Preheat and interpass temperature should be used at 200-300 °C
- The test assembly shall be cooled in the furnace to 300 °C at a rate not exceeding 200 °C/h
- Re-drying: 300-350°C / min. 2h
Current Type
- DC(+)
Welding Positions
Operating Data
| Product Code | Diametré x Length (mm) | Diameter x Length (inch) | Welding Current (A) | Weight g / 100 pcs |
|---|---|---|---|---|
| 3010100849 | ø2,5 x 350 | ø3/32 x 14 | 60 - 90 | 2330 |
| 3010100852 | ø3,2 x 350 | ø1/8 x 14 | 90 - 130 | 3810 |
| 3010100855 | ø4,0 x 450 | ø5/32 x 18 | 120 - 160 | 6680 |