Low Hydrogen Electrode - OPUS CM-15
Standards
| TS EN ISO 3580-A | E CrMo1 B 4 2 H5 |
|---|---|
| EN ISO 3580-A | E CrMo1 B 4 2 H5 |
| AWS A5.5 | E8015-B2 H4 |
Chemical Composition of Weld Metal % (Typical)
| C | Si | Mn | Cr | Mo |
|---|---|---|---|---|
| 0,07 | 0,5 | 0,8 | 1,1 | 0,5 |
Typical Base Material Grades
- 13CrMo4-5, 15CrMo5, 16CrMoV4
- G17CrMo5-5, GS22Mo4, G22CrMo5-4
- ASTM; A193 Gr.B7, A335 Gr.P11
Mechanical Properties
| Yield Strength (N/mm²) | Tensile Strength (N/mm²) | Impact Strength (ISO-V/+20°C) | Elongation ((Lo=5do) (%)) | Heat Treatment |
|---|---|---|---|---|
| min. 460 | 580 - 740 | min. 47J | min. 20 | 680 ±20°C / 1h / furnace down to 300°C / cooling at (air) |
Features and Applications
- Welding of steam boilers and steam pipes made of Cr-Mo alloyed heat resistant steels, cementation steels, nitrided steels
- Resistance of weld metal to operating temperatures of values up to 570°C.
- Weld metal recovery of approx. 125%
- It can be used in position welding with lower heat input
- Usable with short arc in (-) pole for root pass welding with excellent penetration
- Preheat and interpass temperature should be used at 160-190 °C
- The test assembly shall be cooled in the furnace to 300 °C at a rate not exceeding 200 °C/h.
- Re-drying: 300-350°C / min. 2h
Current Type
- DC(+)
Welding Positions
Operating Data
| Product Code | Diametré x Length (mm) | Diameter x Length (inch) | Welding Current (A) | Weight g / 100 pcs |
|---|---|---|---|---|
| 3010100762 | ø2,5 x 350 | ø3/32 x 14 | 80 - 110 | 2190 |
| 3010100765 | ø3,2 x 350 | ø1/8 x 14 | 100 - 140 | 3740 |
| 3010100771 | ø4,0 x 450 | ø5/32 x 18 | 140 - 190 | 6750 |
| 3010100774 | ø5,0 x 450 | ø3/16 x 18 | 190 - 240 | 10020 |