Low Hydrogen Electrode - LASER B 55
Standards
| TS EN ISO 2560-A
|
E 46 5 B 4 2 H5 |
| EN ISO 2560-A
|
E 46 5 B 4 2 H5 |
| AWS A5.1
|
E7018-1 H4 |
Chemical Composition of Weld Metal % (Typical)
Typical Base Material Grades
- S235JR-E295, E335, S235J2G3-S355J2G3, S235JRS1-S235J4S, S315G1S-S355G3S, S255N-S380N, S255NL-S460NL1
- P235T1-P355T1, P235T2, P355T2, P235G1TH, P255G1TH, P235GH-P355GH, P255NH-P355NH
- L210NBL415NB, L290MB-L360MB, API 5L: X42, X46, X52, X56, X60, X65
- GE200-GE300
Mechanical Properties
| Yield Strength (N/mm²) |
Tensile Strength (N/mm²) |
Impact Strength (ISO-V/-50°C) |
Elongation ((Lo=5do) (%)) |
| min. 460 |
530-650 |
min. 47 J |
min. 24 |
Features and Applications
- Suitability for use in out-of-position welding except for welding at vertical down position
- High ductility at low temperatures down to -50°C
- Suitability for use in welding low-purity and high-carbon steels
- Weld deposits with very low hydrogen content
- High-quality weld metals with higher strength values
- Requirement of re-drying for minimum 2 hours at the temperatures between 300°C and 350°C
Current Type
Welding Positions
Operating Data
| Product Code |
Diametré x Length (mm) |
Diameter x Length (inch) |
Welding Current (A) |
Weight g / 100 pcs |
| 3010100411 |
ø2,5 x 350 |
ø3/32 x 14 |
80 - 100 |
2200 |
| 3010100414 |
ø3,2 x 350 |
ø1/8 x 14 |
100 - 140 |
3550 |
| 3010100417 |
ø4,0 x 450 |
ø5/32 x 18 |
130 - 190 |
6570 |
| 3010100420 |
ø5,0 x 450 |
ø3/16 X 18 |
190 - 240 |
10220 |
Approvals