Standards
| TS EN ISO 3581-A
|
E 13 B 2 2 |
| EN ISO 3581-A
|
E 13 B 2 2 |
| AWS A5.4
|
E410-15 |
Chemical Composition of Weld Metal % (Typical)
| C |
Si |
Mn |
Cr |
| 0,07 |
0,7 |
0,8 |
13,5 |
Typical Base Material Grades
- EN; X6Cr13, X6CrAI13, X15Cr13, X10Cr13, G-X10Cr13
- AISI; 410, 420
Mechanical Properties
| Yield Strength (N/mm²) |
Tensile Strength (N/mm²) |
Impact Strength (ISO-V/+20°C) |
Hardness (as welded) (HB) |
Hardness (PWHT)(HB) 750°C/2h/furnace |
| min. 450 |
650-800 |
min. 15 J |
~350 |
200 |
Features and Applications
- 13% Cr used in the joining and surfacing welding of martensitic and martensitic-ferritic steels with 13% Cr and steel casts.( This electrode is also strong at filling in the surfaces of gas, water and steam armatures)
- This 12 Cr alloy is an air-hardening steel. Preheat and postheat treatments are required to achieve welds of adequate ductility for many engineering purposes.
- The most common application of these electrodes is for welding alloys of similar compositions.
- They are also used for surfacing of carbon steels to resist corrosion, erosion, or abrasion.
- Re-drying :300°C - 350°C / min. 2h
Current Type
Welding Positions
Operating Data
| Product Code |
Diametré x Length (mm) |
Diameter x Length (inch) |
Welding Current (A) |
Weight g / 100 pcs |
| 3010101458 |
Ø2,5 x 250 |
Ø3/32 x 10 |
50 - 90 |
1500 |
| 3010101463 |
Ø3,2 x 350 |
Ø1/8 x 14 |
80 - 120 |
3140 |
| 3010101468 |
Ø4,0 x 350 |
Ø5/32 x 14 |
110 - 160 |
4690 |
Approvals