Standards
| TS EN ISO 3581-A
|
E 23 12 L R 3 2 |
| TS EN ISO 3581-A
|
E 23 12 L R 3 2 |
| AWS A5.4
|
E309L-16 |
Chemical Composition of Weld Metal % (Typical)
| C |
Si |
Mn |
Cr |
Ni |
| 0,03 |
0,8 |
0,8 |
23,0 |
12,6 |
Typical Base Material Grades
- Used for buffer layer unalloyed or low alloyed steels, also when joining non-molibdenum-alloyed stainless and carbon steels. Joints and mixed joints between austenitic steels.
- Used for mixed joints between austenitic and heat resistant steels.
Mechanical Properties
| Yield Strength (N/mm²) |
Tensile Strength (N/mm²) |
Impact Strength (ISO-V/+20°C) |
Elongation ((Lo=5do) (%)) |
| min. 440 |
540 - 720 |
min.47 J |
min. 30 |
Features and Applications
- GeKa ELOX R 309L electrodes are widely used in carbon-stainless steel joints. for example, joining mild or low alloy steels with AISI 304.
- If a service temperature above 370 °C or heat treatment is applied after welding dissimilar steels, embrittlement or cracking may occur. This requires procedural control.
- Ferrite content of weld metal is greater than 8 FN and reduces the possibility of intergranular carbide precipitation. This thereby increases the resistance to intergranular corrosion without the use of niobium.
- Re-drying: 120-200ºC / 2 h.
Current Type
Welding Positions
Operating Data
| Product Code |
Diametré x Length (mm) |
Diameter x Length (inch) |
Welding Current (A) |
Weight g / 100 pcs |
| 3010101058 |
ø2,0 x 250 |
ø5/64 x 10 |
50 - 85 |
950 |
| 3010101063 |
ø2,5 x 250 |
ø3/32 x 10 |
60 - 90 |
1540 |
| 3010101073 |
ø3,2 x 350 |
ø1/8 x 14 |
80 - 120 |
3610 |
| 3010101078 |
ø4,0 x 350 |
ø5/32 x 14 |
100 - 160 |
5290 |
Approvals