Standards
| TS EN ISO 3581-A
|
E 13 4 B 6 2 |
| EN ISO 3581-A
|
E 13 4 B 6 2 |
| AWS A5.4
|
E410NiMo-25 |
Chemical Composition of Weld Metal % (Typical)
| C |
Si |
Mn |
Cr |
Ni |
Mo |
| 0,05 |
0,3 |
0,5 |
11,5 |
4,5 |
0,5 |
Typical Base Material Grades
- X5CrNi 13 4, G-X5CrNi 13 4, X6Cr 13, G-X5CrNi 13 6
Mechanical Properties
| Yield Strength (N/mm²) |
Tensile Strength (N/mm²) |
Impact Strength (ISO-V/+20°C) |
Elongation ((Lo=5do) (%)) |
Hardness (as welded) (HB) |
| min. 600 |
800-980 |
min. 47 J |
min. 15 |
~270 |
Features and Applications
- Basic coated electrode for welding similar corrosion-resistant, martensitic and martensitic-ferritic rolled, forged and cast steels
- Used in the construction of hydroturbines, compressors and steam power plants
- Resistant to corrosion caused by water, steam and sea water atmosphere
- Excellent slag removability and smooth bead appearance
- Metal recovery approx. 130% Out-of-position weldability
- Preheating and interpass temperatures of thick-walled components 100°C-180°C
- Tempering temperature 580°C-620°C / 2 hours in the air cooling.
- Re-drying: 300-350°C / min. 2 h
Current Type
Welding Positions
Operating Data
| Product Code |
Diametré x Length (mm) |
Diameter x Length (inch) |
Welding Current (A) |
Weight g / 100 pcs |
| 3010101488 |
Ø2,5 x 250 |
Ø3/32 x 14 |
70 - 110 |
1960 |
| 3010101493 |
Ø3,2 x 350 |
Ø1/8 x 14 |
110 - 150 |
3630 |
| 3010101498 |
Ø4,0 x 350 |
Ø5/32 x 14 |
150 - 190 |
5550 |