Standards
| TS EN ISO 3581-A
|
E 22 9 3 N L R 3 2 |
| TS EN ISO 3581-A
|
E 22 9 3 N L R 3 2 |
| AWS A5.4
|
E2209-17 |
Chemical Composition of Weld Metal % (Typical)
| C |
Si |
Mn |
Cr |
Ni |
Mo |
N |
| 0,03 |
0,50 |
0,9 |
22,0 |
10,0 |
2,7 |
0,12 |
Typical Base Material Grades
- X2CrNiMoN22-5-3, X2CrNiN23-4, X2CrNiMoN22-5-3 ile X10CrNiMoNb18-12
- P235GH/ P265GH, S255N, P295GH, S355N, 16Mo3
Features and Applications
- Suitability to joint same alloyed, similar alloyed, ferritic-austenitic steels with higher tensile strength.
- Excellent weldability
- Very high resistance to stress corrosion cracking and pitting resistance.
- Re-drying : 250-300°C / min. 2h
- Preheating and interpass temperature max. 150 °C
Mechanical Properties
| Yield Strength (N/mm²) |
Tensile Strength (N/mm²) |
Impact Strength (ISO-V/+20°C) |
Elongation ((Lo=5do) (%)) |
| min. 520 |
690-850 |
min. 47 J |
min. 20 |
Current Type
Welding Positions
Operating Data
| Product Code |
Diametré x Length (mm) |
Diameter x Length (inch) |
Welding Current (A) |
Weight g / 100 pcs |
| 3010101533 |
Ø2,5 x 250 |
Ø3/32 x 10 |
50 - 90 |
1410 |
| 3010101538 |
Ø3,2 x 350 |
Ø1/8 x 14 |
80 - 120 |
3540 |
| 3010101543 |
Ø4,0 x 350 |
Ø5/32 x 14 |
110 - 160 |
5200 |