Standards
| EN ISO 3581-A
|
E Z 19 13 4 L R 1 2 |
| TS EN ISO 3581-A
|
E Z 19 13 4 L R 1 2 |
| AWS A5.4
|
E317L-16 |
Chemical Composition of Weld Metal % (Typical)
| C |
Si |
Mn |
Cr |
Ni |
Mo |
| <0,04 |
0,80 |
0,9 |
18,7 |
12,5 |
3,2 |
Typical Base Material Grades
- CrNiMo(N) steels with increased Mo-content like grade AISI 316LN/317LN or corrosion resistant claddings on mild steels
- AISI; 316LN, 317L, 317LN
Features and Applications
- Rutile coated alloyed-core wire electrode for corrosion resistant CrNi steels of increased Mo-contents
- Reduces the possibility of intergranular carbide precipitation, providing increase in resistance to intergranular corrosion without use of stabilizers such as Niobium or Titanium
- Re-drying: 120-200ºC / 2 h.
Mechanical Properties
| Yield Strength (N/mm²) |
Tensile Strength (N/mm²) |
Impact Strength (ISO-V/+20°C) |
Elongation ((Lo=5do) (%)) |
| min. 400 |
570-700 |
min. 47 J |
min. 30 |
Current Type
Welding Positions
Operating Data
| Product Code |
Diametré x Length (mm) |
Diameter x Length (inch) |
Welding Current (A) |
Weight g / 100 pcs |
| 3010101318 |
Ø2,5 x 250 |
Ø3/32 x 10 |
50 - 90 |
1570 |
| 3010101323 |
Ø3,2 x 350 |
Ø1/8 x 14 |
80 - 120 |
3560 |
| 3010101328 |
Ø4,0 x 350 |
Ø5/32 x 14 |
110 - 160 |
5100 |