Stainless Steel Electrode - ELOX B 307
Standards
| TS EN ISO 3581-A
|
E 18 8 Mn B 2 2 |
| EN ISO 3581-A
|
E 18 8 Mn B 2 2 |
| AWS A5.4
|
~E307-15 |
Chemical Composition of Weld Metal % (Typical)
| C |
Si |
Mn |
Cr |
Ni |
| 0,1 |
0,7 |
6,0 |
18,5 |
8,6 |
Typical Base Material Grades
- DIN; X6Cr13, X6CrAl13, X10Cr13, X8Cr17, X20Cr13, X10CrAl7, X10CrAl13, X15Cr13, X22CrNi17, X5CrNi13-4, X8CrT,17, G-X20Cr14, G-X8CrNi13, G-X30CrSi6
- AISI; 405, 410, 420, 430, 430Ti, 431, 440, 502
Mechanical Properties
| Yield Strength (N/mm²) |
Tensile Strength (N/mm²) |
Impact Strength (ISO-V/+20°C) |
Elongation ((Lo=5do) (%)) |
| min. 390 |
580-750 |
min 80J |
min. 35 |
Features and Applications
- Joint welding of different metals with each other.
- Electrodes of this composition are used primarily for moderate strength welds with good crack resistance between dissimilar steels such as austenitic manganese steel and carbon steel forgings or castings.
- Dissimilar joints, tough buffer and intermediate layers prior to hardfacing, 14Mn-steels, 13 – 17% Cr and heat resistant Cr and austenitic steels up to 850ºC, armor plates, high carbon and quenched and tempered steels, surfacing of gears, valves, turbine blades, etc. For joint welding of unalloyed / low-alloyed or Cr steels with high-alloyed Cr and CrNi-steels. Welding of austenitic high manganese steels and with other steels.
- Resistance of weld metal to corrosion, wear, thermal shocks and working temperatures between -100 °C and +500 °C
Current Type
Welding Positions
Operating Data
| Product Code |
Diametré x Length (mm) |
Diameter x Length (inch) |
Welding Current (A) |
Weight g / 100 pcs |
| 3010100893 |
ø2,5 x 250 |
ø3/32 x 10 |
60 - 80 |
1280 |
| 3010100898 |
ø3,2 x 350 |
ø1/8 x 14 |
80 - 100 |
3170 |
| 3010102108 |
ø4,0 x 350 |
ø5/32 x 14 |
110 - 140 |
4900 |
| 3010100903 |
ø5,0 x 350 |
ø3/16 x 14 |
140 - 160 |
7650 |