Standards
| TS EN ISO 3581-A
|
E 19 9 H R 3 2 |
| EN ISO 3581-A
|
E 19 9 H R 3 2 |
| AWS A5.4
|
E308H-16 |
Chemical Composition of Weld Metal % (Typical)
| C |
Si |
Mn |
Cr |
Ni |
| 0,07 |
0,7 |
0,8 |
19,0 |
10,4 |
Typical Base Material Grades
- DIN; X5CrNi18 -10, X6CrNiTi18-10, X6CrNiNb18-10, X8CrNiTi18-10, X7CrNi18-9
- AISI; 304, 304H, 321, 321H, 347, 347H
Features and Applications
- Electrode with rutile coating on alloyed core-wire
- Applicability in welding Cr-Ni alloyed austenitic high temperatures steels
- Usability in welding at all positions except for vertical downward position
- Applicability in joint welding and surfacing of heat resisting similar type steels and steel casting
- Serviceability at temperatures of values up to 700°C
- The deposit is resistant to embrittlement and scaling
- Creep resistance at high temperatures being higher than that of the electrode GeKa ELOX R 308 L
- Preheat and interpass temperature shold not exceed 150 °C.
- Re-drying: 120-200ºC / 2 h.
Mechanical Properties
| Yield Strength (N/mm²) |
Tensile Strength (N/mm²) |
Impact Strength (ISO-V/+20°C) |
Elongation ((Lo=5do) (%)) |
| min. 355 |
550 - 650 |
min. 47 J |
min. 35 |
Current Type
Welding Positions
Operating Data
| Product Code |
Diametré x Length (mm) |
Diameter x Length (inch) |
Welding Current (A) |
Weight g / 100 pcs |
| 3010101008 |
ø2,5 x 250 |
ø3/32 x 10 |
50 - 80 |
1490 |
| 3010101013 |
ø3,2 x 350 |
ø1/8 x 14 |
80 - 110 |
3430 |
| 3010101018 |
ø4,0 x 350 |
ø5/32 x 14 |
110 - 140 |
5060 |