Stainless Steel Electrode - ELOX R 307
Standards
| TS EN ISO 3581-A
|
E 18 8 Mn R 3 2 |
| EN ISO 3581-A
|
E 18 8 Mn R 3 2 |
| AWS A5.4
|
~E307-16 |
Chemical Composition of Weld Metal % (Typical)
| C |
Si |
Mn |
Cr |
Ni |
| 0,11 |
1,0 |
4,5 |
19,0 |
8,5 |
Typical Base Material Grades
- DIN; X7Cr13, X7CrAl13, X10Cr13, X8Cr17, X20Cr13, X10CrAl13, X10CrAl7, X15Cr13, X22CrNi17, X5CrNi13 4, X8CrTi 17, G-X20Cr14, G-X8CrNi13, G-X30CrSi8
- AISI; 405, 410, 420, 430, 430Ti, 431, 440, 502
Mechanical Properties
| Yield Strength (N/mm²) |
Tensile Strength (N/mm²) |
Impact Strength (ISO-V/+20°C) |
Elongation ((Lo=5do) (%)) |
| min. 390 |
600-770 |
min. 47 J |
min. 30 |
Features and Applications
- Dissimilar joints, tough buffer and intermediate layers prior to hardfacing, 14Mn-steels, 13 – 17% Cr and heat resistant Cr and austenitic steels up to 850ºC, armor plates, high carbon and quenched and tempered steels, surfacing of gears, valves, turbine blades, etc. For joint welding of unalloyed / low-alloyed or Cr steels with high-alloyed Cr and CrNi-steels. Welding of austenitic high manganese steels and with other steels.
- Joint welding and filler welding of difference metal with each other
- Electrode coating of rutile character
- Austenitic weld metal with resistance to thermal shocks
- Maintenance of toughness at temperatures down to -100°C
- The most important advantages to use with Alternating Current welding machine. Electrodes should be used after re-drying at 300 ° C for at least 2 hours.
Current Type
Welding Positions
Operating Data
| Product Code |
Diametré x Length (mm) |
Diameter x Length (inch) |
Welding Current (A) |
Weight g / 100 pcs |
| 3010100908 |
ø2,5 x 250 |
ø3/32 x 10 |
60 - 80 |
1440 |
| 3010100913 |
ø3,2 x 350 |
ø1/8 x 14 |
80 - 110 |
3300 |
| 3010100918 |
ø4,0 x 350 |
ø5/32 x 14 |
110 - 140 |
4940 |
| 3010100923 |
ø5,0 x 350 |
ø3/16 x 14 |
140 - 160 |
7520 |
Approvals